| Customization: | Available |
|---|---|
| After-sales Service: | 1year |
| Warranty: | 1year |
|
Still deciding? Get samples of US$ 0/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Process | Aluminum Die casting, Squeeze casting+T6, Iron Sand Casting, Gravity Casting, Zinc Die Casting, Investment Casting, Copper Casting, CNC Machining, In-house Tooling. |
| Equipment | Cold chamber aluminum die casting & squeeze casting machines: 200T/280T/400T/600T/800T/1100T. CNC machining centers, CNC gantry machining centers, CNC turning, CNC lathes, CNC milling, CNC drilling, CNC grinding, and EDM machines. |
| Material | For Aluminum Die Casting: A319, A356, A360, A369, A380, A383, A384, A413, A535, 44300, 44300, 46000, AlSi9Mg, AlSi9Cu3, ADC12, ZL102, ZL104, ZL108, Zamak2,3,5,7 etc. For Aluminum Squeeze Casting: A356+T6, A356.2+T6, AlSi9Mg+T6, ZL108+T6, AlTi-Alloy+T6. |
| Surface | Trimming, Deburring, Polishing, Shot Blasting, Sand Blasting, Tumbling, Powder Coating, Anodizing, Chrome Plating, Zinc Plating, Electrophoresis, Passivation, Chemical Coating. |
| Software Assistance | Pro-e/Solidworks/UG/Auto CAD/CATIA |
| Product Applications | Automotive, Bicycle, Motorcycle, Aerospace, Machinery, Household, Electric Appliances, Oil and Gas, Fluid Control, LED Lighting, Medical Instruments, Telecom, etc. |
CEX Casting was established in 1995. We are a fully integrated manufacturer of aluminum die casting, squeeze casting, CNC machining, and in-house tooling services.
We have applied for an invention patent for our newly developed aluminum squeeze casting process. Unlike conventional die castings, squeeze castings come with zero internal porosity, higher density, and similar mechanical properties to aluminum forgings, making them suitable for industries requiring lightweight and high-strength features, especially in the automotive industry.
We manufacture high-quality and precise aluminum casting blanks that comply with specific requirements. We also offer surface finish and CNC machining services to ensure that the casting blanks are prepared and finished to the customer's expectations.
Our products are mainly exported to North American and European markets. We have rich experience cooperating with foreign customers and in-depth knowledge of their requirements.
| Our Quality Inspection Instruments | |
| Material Composition | Orient Spectrometer, Chemical Analysis |
| Dimensions and Tolerances | Coordinate Measuring Machine (CMM), Micrometer, Vernier Caliper, Full Range Pin Gauge/Gauge |
| Mechanical Properties (Strength, Hardness, Density) | Tensile Testing Machine, Hardness Tester, Density Tester |
| Internal Structure (Porosity) | X-Ray Machine, Ultrasonic Testing, Destructive Testing, Metallographic Examination |
We have found a solution to effectively solve the problem of porosity defects in traditional aluminum castings--our patented squeeze casting process.
CEX started to research and develop the squeeze casting process in 2015. As a China professional squeeze casting manufacturer, we own one squeeze casting manufacturing base with the patented squeeze casting process and equipment.
Our aluminum squeeze casting parts can eliminate defects such as internal porosity and shrinkage and have a dense internal organization.
Squeeze casting is a more advanced process than conventional aluminum casting methods.
The squeeze casting process can eliminate defects that exist in the traditional casting processes such as porosity and shrinkage, and the internal structure of the casting is more dense. Heat treatment and welding are acceptable.
Better Mechanical Properties: the strength of the heat-treated squeeze castings is significantly higher and can reach strengths close to those of forged aluminum parts.
Better Sealing Performance: because the presence of pores is eliminated, the surface of the squeeze castings can be machined to a very high finish, free of pore defects, thus ensuring excellent sealing performance without causing leaks.
Can Be Welded: conventional aluminum castings often contain microscopic pores and voids within the material. These porosities can act as potential weak points and will lead to defects and reduce welding integrity. Squeeze casting parts without internal porosity can avoid these problems.
| Aluminum Alloy Type | Grade | Processing | Heat Treatment State | Mechanical Properties | |
| σb/Mpa | δ/% | ||||
| Al-Si Casting Aluminum Alloy | ZL115 | Squeeze Casting | Casting (F) | 280-290 | 7-8 |
| Quenching and Timing (T6) | 300-340 | ≥7 | |||
| Metal Casting | Quenching (T4) | 270 | 6 | ||
| ZL106 | Squeeze Casting | Quenching and Timing (T5) | 351 | 11.3 | |
| Metal Casting | Quenching and Timing (T5) | ≥235 | ≥0.5 | ||
| A356.2 (US) | Squeeze Casting | Casting (F) | 270-280 | 6-8 | |
| Quenching and Timing (T6) | 296-310 | 10-14 | |||
| Metal Casting | Quenching and Timing (T6) | 283-303 | 3-5 | ||
| ADC12 (JP) | Pressure Casting | Casting | 194 | 1.5 | |
| Squeeze Casting | Casting | 288 | 3.5 | ||
| Quenching and Timing (T6) | 316-423 | 4.4-5.7 | |||
| Al-Cu Casting Aluminum Alloy | ZL201 | Squeeze Casting | Quenching and Timing (T5) | 449 | 16.7 |
| Metal Casting | Quenching and Timing (T5) | 329 | 2.6 | ||
| Al-Cu Deforming Aluminum Alloy | 2A14 | Squeeze Casting | Quenching and Timing | 496 | 5.8 |
| Forging | Quenching and Timing | ≥353 | ≥4 | ||
| Al-Zn-Mg-Cu Deforming Aluminum Alloy | 7A04 | Squeeze Casting | Quenching and Timing | 552 | 5.5 |
| Forging | Quenching and Timing | ≥441 | ≥3 | ||
| Items | Squeeze Casting | Forging | Gravity Casting | High Pressure Casting | Low Pressure Casting |
| Surface | Fine | Fine | Bad | Fine | Middle |
| Roughness | Ra3.2-1.6 | Ra3.2-1.6 | Ra6.3-3.2 | Ra3.2-1.6 | Ra6.3-3.2 |
| Internal Tissue | Fine Particles and Tight Tissue | Fine Particles and Tight Tissue | Rough Particles and Loose Tissue | Uneven Particles and Loose Tissue | Uneven Particles and Loose Tissue |
| Heat Treatment | T6 | T6 | T6 | Not | T6 |
| Structural | Complexity | Simple | Complexity | Complexity | Simple |
| Precision | High | Middle | Middle | High | Low |
| Machining Allowance | Less | More | More | Less | More |
| Efficiency | High | Low | Low | High | Low |
| Mechanical Behavior | Close to Forging | High | Middle | Low | Low |